ชื่อเรื่อง: Fatigue Resistance of Cast-on Implant Abutment Fabricated with Three Different Alloys
ผู้แต่ง: Puengpaiboon U.
Didron P.P.
Keywords: cast-on abutment
dental implant
fatigue resistance
mechanical failure
วันที่เผยแพร่: 2023
สำนักพิมพ์: Georg Thieme Verlag
บทคัดย่อ: Objectives This study aimed to evaluate fatigue resistance of cast-on implant abutment using three alloys. Materials and Methods Forty specimens of implant-supported crowns were prepared; Group 1 (TA) stock titanium abutments, Group 2 (GS) abutment cast with 40% gold alloy, Group 3 (GP) abutment cast with palladium alloy, and Group 4 (CN) abutment cast with nickel-chromium alloy. Specimens were cyclic loaded at 20 Hz, starting from 200 N (5,000 cycles), followed by stepwise loading of 400, 600, 800, 1,000, 1,200, 1,400, 1,600, and 1,800 N (30,000 cycles/step). Specimens were loaded until failure or reached 245,000 cycles. Statistical Analysis The withstand cycles were analyzed using one-way analysis of variance and Weibull survival analysis. Fracture surfaces were examined using scanning electron microscopy. Results The results of withstand cycles were TA (189,883 ± 22,734), GS (195,028 ± 22,371), GP (187,662 ± 22,555), and CN (200,350 ± 30,851). The statistical analysis showed no significant difference between the groups (p = 0.673). Conclusion Although CN has higher Weibull characteristic strength which means greater durability, its lower Weibull modulus demonstrated less structural reliability. Consistent failures at implant fixture level were also found in CN group. © 2023 Georg Thieme Verlag. All rights reserved.
URI: https://www.scopus.com/inward/record.uri?eid=2-s2.0-85125755017&doi=10.1055%2fs-0041-1742124&partnerID=40&md5=d22abf2eb97f032c22d4382d0752b70f
https://ir.swu.ac.th/jspui/handle/123456789/29304
Appears in Collections:Scopus 2023

Files in This Item:
There are no files associated with this item.


Items in SWU repository are protected by copyright, with all rights reserved, unless otherwise indicated.