ชื่อเรื่อง: Characterization of LiNbO3 powder prepared by citrate gel method
ผู้แต่ง: Onnom S.
Wongratanaphisn D.
Supaphol P.
Udomsamuthirun P.
Nilkamjon T.
Radrang S.
Sonkrua S.
Payoogthum S.
Keywords: Average particle sizes
Calcination temperatures
Chemical compositions
Citrate gel method
Distilled waters
FTIR
LiNbO3 powder
Lithium niobate
Sem
Starting materials
Stoichiometric ratios
Synthesized powders
Tem
XRD
Acids
Calcination
Citric acid
Dissolution
Fourier transform infrared spectroscopy
Gelation
Gels
Intelligent materials
Lithium
Nanostructured materials
Niobium
Niobium compounds
Powders
Thermal effects
Functional materials
วันที่เผยแพร่: 2008
บทคัดย่อ: Lithium niobate powder (LiNbO3) were synthesized by citrate gel method using LiNO3, Nb2O5, citric acid and HF as starting materials. LiNO3 was dissolved in distilled water that activated into LiOH. Nb2O5 was dissolved in minimum amount of HF at 37°C for 20 h. that activated into NbF5. Then citric acid, LiOH, and NbF5 were mixed in stoichiometric ratio. On heating at 100°C for 3-4 h. a yellowish gel is formed. Lithium niobate powders were obtained after calcination at 550-700°C. The effect of calcination temperature at various temperatures ranging from 550°C to 700°C were investigated. The phase and chemical composition of the synthesized powders were characterized by using XRD, SEM, TEM, FTIR and EDX. We found that the lithium niobate crystallize phase formed when the calcination temperature at 650°C with average particle size of around 100 nm. © 2008 Trans Tech Publications, Switzerland.
URI: https://ir.swu.ac.th/jspui/handle/123456789/14805
https://www.scopus.com/inward/record.uri?eid=2-s2.0-62949156376&partnerID=40&md5=6ad8b83538d6d981fb73b0f1d569ca38
ISSN: 10226680
Appears in Collections:Scopus 1983-2021

Files in This Item:
There are no files associated with this item.


Items in SWU repository are protected by copyright, with all rights reserved, unless otherwise indicated.