ชื่อเรื่อง: Effects of aromatic carboxylic dianhydrides on thermomechanical properties of polybenzoxazine-dianhydride copolymers
ผู้แต่ง: Jubsilp C.
Ramsiri B.
Rimdusit S.
Keywords: Benzophenonetetracarboxylic dianhydride
Benzoxazine
Bisphenol A
Char yield
Copolymer films
Cross-link densities
Dianhydrides
Ester linkages
Hydroxyl groups
Nitrogen atmospheres
Polybenzoxazine
Pyromellitic dianhydride
Thermal curing
Thermal degradation temperatures
Thermomechanical properties
Phenols
Copolymers
วันที่เผยแพร่: 2012
บทคัดย่อ: Enhanced thermomechanical properties of bisphenol-A based polybenzoxazine (PBA-a) copolymers obtained by reacting bisphenol-A-aniline-type benzoxazine (BA-a) resin with three different aromatic carboxylic dianhydrides, i.e., pyromellitic dianhydride (PMDA), 3,3',4,4' biphenyltetracarboxylic dianhydride (s-BPDA), or 3,3',4,4' benzophenonetetracarboxylic dianhydride (BTDA) were reported. Glass transition temperature (T g), of the copolymers was found to be in the order of PBA-a:PMDA>PBA-a:s-BPDA>PBA-a:-BTDA. The difference in the T g of the copolymers is related to the rigidity of the dianhydride components. Furthermore, the T g of PBA-a:BTDA, PBA-a:s-BPDA, and PBA-a:BTDA films was observed to be significantly higher than that of the neat PBA-a owing to the enhanced crosslink density by the dianhydride addition. This greater crosslink density results from additional ester linkage formation between the hydroxyl group of PBA-a and the anhydride group of dianhydrides formed by thermal curing. Moreover, the copolymers exhibit enhanced thermal stability with thermal degradation temperature (T d) ranging from 410°C to 426°C under nitrogen atmosphere. The char yield at 800°C of the copolymers was found to be remarkably greater than that of the neat PBA-a with a value up to 60% vs. that of about 38% of the PBA-a. Toughness of the copolymer films was greatly improved compared to that of the neat PBA-a. POLYM. ENG. SCI., 2012. © 2012 Society of Plastics Engineers Copyright © 2012 Society of Plastics Engineers.
URI: https://ir.swu.ac.th/jspui/handle/123456789/14300
https://www.scopus.com/inward/record.uri?eid=2-s2.0-84863721716&doi=10.1002%2fpen.23107&partnerID=40&md5=8c0a83e11bbdd0f34d54f558bd7b1d7d
ISSN: 323888
Appears in Collections:Scopus 1983-2021

Files in This Item:
There are no files associated with this item.


Items in SWU repository are protected by copyright, with all rights reserved, unless otherwise indicated.