Publication: Electric and Magnetic Properties of Bi0.80Ba0.20FeO3-Doped Ba0.85Ca0.15Ti0.90Zr0.10O3 Ceramics Prepared via the Solid-State Combustion Technique
0
0
Issued Date
2022
Resource Type
Language
eng
File Type
application/pdf
ISSN
18626300
Rights Holder(s)
มหาวิทยาลัยศรีนครินทรวิโรฒ
Bibliographic Citation
Journal of Cosmetic Dermatology. Vol 21, No.10 (2022), p.5092-5097
Suggested Citation
Thawong P., Prasertpalichat S., Suriwong T., Pinitsoontorn S., Vittayakorn N., Pulphol P., Bongkarn T. Electric and Magnetic Properties of Bi0.80Ba0.20FeO3-Doped Ba0.85Ca0.15Ti0.90Zr0.10O3 Ceramics Prepared via the Solid-State Combustion Technique. Journal of Cosmetic Dermatology. Vol 21, No.10 (2022), p.5092-5097. doi:10.1002/pssa.202200418 Retrieved from: https://hdl.handle.net/20.500.14740/9230
Abstract
Lead-free (1−x)Ba0.85Ca0.15Ti0.90Zr0.10O3–xBi0.80Ba0.20FeO3 [(1−x)BCTZ–xBBF] ceramics, with BBF content (x) between 0 and 0.4, are prepared via the solid-state combustion technique. The effect of BBF content on the phase formation, microstructure, and electric and magnetic properties of BCTZ is studied. From the Rietveld refinement analysis, the BCTZ ceramic shows coexisting orthorhombic and tetragonal phases, with a ratio of 35.4:64.6 and the percentage of the tetragonal phase continuously increases when x increases from 0.02 to 0.1, and becomes purely tetragonal at x ≥ 0.2. When x increases, the average grain size, density, and relative density continuously decrease while the unit cell volume enlarges. The dielectric constant at room temperature (εR) tends to decrease while the dielectric loss at room temperature (tan δR) increases with increased BBF content. For x = 0, a pure BCTZ ceramic, a well-saturated P–E loop is observed with a polarization (Pr) and coercive field (Ec) of 8.94 μC cm−2 and 4.06 kV cm−1, respectively. The ferroelectricity drastically decreases with x = 0.02. For x ≥ 0.06, the leakage current increases, which suppresses the ferroelectricity. With no BBF content (x = 0), the ceramic has diamagnetic properties that change to paramagnetic properties with x = 0.02–0.06 and finally to ferromagnetic properties when the BBF increases between 0.10 and 0.40. For x = 0.10–0.40, the remnant magnetization (Mr) continuously increases. © 2022 Wiley-VCH GmbH.