Publication: The Microstructure and Diffusion Transformation of Precipitation-Hardened Sterling Silver for Jewelry Application
19
0
Issued Date
2025-01-01
Resource Type
ISSN
16628969
eISSN
16620356
DOI
Scopus ID
2-s2.0-85217699651
Journal Title
Advances in Science and Technology
Volume
158
Start Page
55
End Page
62
Rights Holder(s)
SCOPUS
Bibliographic Citation
Advances in Science and Technology Vol.158 (2025) , 55-62
Suggested Citation
Denjarukul P., Sinpromma S., Peerawat A., Jintakosol T., Yongperakul C., Wongpreedee K. The Microstructure and Diffusion Transformation of Precipitation-Hardened Sterling Silver for Jewelry Application. Advances in Science and Technology Vol.158 (2025) , 55-62. 62. doi:10.4028/p-10hQwX Retrieved from: https://hdl.handle.net/20.500.14740/20708
Author's Affiliation
Corresponding Author(s)
Other Contributor(s)
Abstract
Sterling silver commonly uses copper as its primary alloying element, which enhances hardness. However, the presence of copper can cause a fire stain—a red spot microstructure—leading to tarnishing issues. This research focuses on reducing the copper content and developing suitable processes to enhance hardness through the use of three different alloy compositions within the AgCu and AgCuZnNi systems: Alloy SA (92.5 wt% Ag - 7.5 wt% Cu), Alloy A (93.5 wt% Ag - 5.01 wt% Cu - 0.79 wt% Zn - 0.70 wt% Ni), and Alloy B (94.5 wt% Ag - 4.24 wt% Cu - 0.63 wt% Zn - 0.63 wt% Ni). Precipitation hardening was measured at temperatures of 250 °C, 350 °C, and 450 °C for various durations ranging from 15 to 180 minutes. The results demonstrated an improvement in hardness, increasing from 60-70 HV to 120-160 HV after the heat treatment, with optimal results achieved for Alloy B at a temperature of 350 °C for one hour. This refined alloy composition presents a viable alternative, offering reduced copper content while maintaining enhanced mechanical strength and long-term durability post-heat treatment. Furthermore, the CIELAB test confirmed that Alloy B exhibits superior tarnish resistance. The composition and optimized process outlined in this research can serve as a guideline for producing sterling silver for commercial applications.