ชื่อเรื่อง: | Effects of precursor concentration on hexagonal structures of ZnO nanorods grown by aqueous solution method |
ผู้แต่ง: | Limnonthakul P. Chananonnawathorn C. Aiempanakit K. Kaewkhao J. Eiamchai P. Horprathum M. |
Keywords: | Aqueous solution methods Field emission scanning electron microscopy Hexagonal structures Hexagonal wurtzite structure Physical morphology Precursor concentration ZnO nanorod ZnO nanorod arrays Enamels Solutions X ray diffraction analysis Zinc oxide Zinc sulfide Nanorods |
วันที่เผยแพร่: | 2013 |
บทคัดย่อ: | The ZnO nanorods were fabricated on top of the seeded gold layer by the aqueous solution method with the solution of zinc nitrate and hexamethylenetetramine (HTMA) at 90°C for 24 hours. The variety of the ZnO nanorods were prepared and investigated based on the precursor concentrations, in a range of 1 to 40 mM. The physical morphologies and crystal structures were characterized by field-emission scanning electron microscopy (FE-SEM) and X-ray diffractometry (XRD), respectively. The results showed that, with the small precursor concentrations, the lateral growth of the nanorods was highly significant when compared to their axial growth. The precursor concentration of 20 mM was best optimized for the preparation of the ZnO nanorod arrays with the hexagonal structures at the highest rod diameter and length. At the higher concentrations, although the nanorod size remained nearly constant, the length was however rapidly decreased. Further analyses also proved that, with the increased precursor concentrations, the number density of the ZnO nanorods was progressively increased along with the more complete hexagonal wurtzite structures. © (2013) Trans Tech Publications, Switzerland. |
URI: | https://ir.swu.ac.th/jspui/handle/123456789/13980 https://www.scopus.com/inward/record.uri?eid=2-s2.0-84884912457&doi=10.4028%2fwww.scientific.net%2fAMR.770.120&partnerID=40&md5=37d56a1236e528945d5a18315e266866 |
ISSN: | 10226680 |
Appears in Collections: | Scopus 1983-2021 |
Files in This Item:
There are no files associated with this item.
Items in SWU repository are protected by copyright, with all rights reserved, unless otherwise indicated.